Products

TMT115-WEBSTER HARDNESS TESTERS

Category: Hardness tester

 

WEBSTER HARDNESS TESTERS

 

 

 

W Series Webster Tester is a portable instrument which can on-site test soft metals quickly. The Webster Hardness Tester is used to inspect the result of heat treatment, to sort the materials in the warehouse, and to test the long workpieces inconvenient taken to the lab. The Webster hardness tester is very suitable for quality inspection of batch products one by one in the production field. The hardness value can be read directly on the indicator dial.

MODEL B Webster Hardness Tester is the choice of virtually every aluminum extrusion manufacturer. This first hardness tester specially crafted for aluminum has improved the aluminum industry.

A test can be completed by one press.

Model W-20 equivalent to Model B Tester

Models for testing brass, copper and mild steel respectively

Modification models for testing thick pieces or slim tubings

Tests sheets, extrusions, pipes

Very fast, very simple and very portable

Small indentation

Conforms to ASTM B647

Recommended in YS/T420.

Webster Hardness Tester for Aluminum Alloys W-20, W-20a, W-20a, W-20b

MODEL

Dimension of specimen

NET WEIGHT

APPLICATIONS

W-20

0.8- 6mm

0.5KG

regular type for aluminum alloy profile, pipe and sheet

W-20a

0.8--13mm

0.5KG

thick wall aluminum alloy material

W-20b

Min Dia: 6mm

0.5KG

aluminum alloy pipe of small diameter and aluminum alloy

Webster Hardness Tester for Copper Alloys W-B75, W-B75b, W-BB75, W-BB75b

MODEL

Dimension of specimen

NET WEIGHT

APPLICATIONS

W-B75

Thickness:

0.8 - 6mm

0.5KG

extra-hard aluminum, brass

W-B75b

Min Dia: 6mm

0.5KG

slim extra-hard aluminum or brass pipe

W-BB75

Thickness: 0.8--6mm

0.5KG

copper and soft copper alloys such as annealed brass

W-BB75b

Min Dia: 6mm

0.5KG

copper or annealed brass pipe

Webster Hardness Tester for Mild Steel W-B92

MODEL

Thickness of specimen

NET WEIGHT

APPLICATIONS

W-B92

0.8 - 6mm

0.5KG

soft steel materials not exceeding 230 HV, such as cold rolled sheet, hot rolled sheet and galvanized sheet etc.

 

B+ Webster Aluminium Hardness Tester

 

            The Webster hardness tester is a portable instrument for fast hardness inspection of aluminum alloy. The hardness value can be directly read on the dial after one simple press on the handle. The Webster hardness tester conforms to ASTM B647. It is suitable for testing the mechanical performance of the result of heat treatment of aluminum extrusions, sheets and tubes. The typical application is 100% quality inspection as acceptance check at the production line, in the warehouse or in the office.

The new B+ Webster hardness tester features a wear-free nanotechnology indentor. The indentor is so hard that it cuts glass like a diamond tool. It has a guaranteed life of three years, and its actual life is more than five years under normal use condition. This is the first hardness tester indentor in the industry to have a warranty.

A major factor affecting the accuracy of most Webster testers is that when exerting excessive force on the handles after the bottom is felt, the indicator will continue to move half or one graduation higher. This is no longer a problem for the redesigned B+ Tester, and the reading is consistent for all operators.

Features

            Wear-free indentor w/ 3 yr warranty

            Less frequent calibration required

            More consistent reading

            Oxide coated aluminum handles

            Exchangeable indicator dial assembly

Specifications

            Range: 0-20 HW (40-100HRE)

            Resolution: 0.5 HW

            Capacity: 6mm (Expendable to 13mm)

            Net weight: 0.47kg

 

Ask about this product